Mould for a composite material part coated with a stripping product

ABSTRACT

The invention relates to a mold for making a composite material part, the mold being coated in a stripping composition. The stripping composition comprises: 100 parts by weight of a base ingredient consisting in epoxy polydimethylsiloxane; 0.5 to 10 parts by weight of a polymerization agent for polymerizing the base ingredient and constituted by a diaryliodonium salt; not more than 30 parts by weight of an anti-adhesion modulator constituted by a silicone polymer; and not more than 40 parts by weight of an anti-stick agent making the composition less tacky prior to polymerization and constituted by at least one vinyl ether compound.

The present invention relates to a mold for making a composite material part, the mold being coated in a stripping composition. Although not exclusively, the present invention applies particularly to helicopter blades or to helicopter blade elements, which are usually manufactured by molding a composite material.

In order to make it easier to extract such blades or blade elements from the mold after polymerization, it is conventional initially to apply a stripping composition over the entire surface of the mold.

Known stripping compositions contain a large proportion of solvent, and as a result present numerous drawbacks, such as the large quantities that need to be used and the volatile organic compounds that are dumped into the environment.

An object of the present invention is to remedy those drawbacks. The invention relates to a mold coated in a solvent-free anti-adhesive stripping composition that is particularly effective.

To this end, according to the invention, a mold for making a composite material part is coated in a stripping composition comprising:

-   -   100 parts by weight of a base ingredient consisting in epoxy         polydimethylsiloxane;     -   0.5 to 10 parts by weight of a polymerization agent for         polymerizing the base ingredient and constituted by a         diaryliodonium salt;     -   not more than 30 parts by weight of an anti-adhesion modulator         constituted by a silicone polymer; and     -   not more than 40 parts by weight of an anti-stick agent making         the composition less tacky prior to polymerization and         constituted by at least one vinyl ether compound.

Preferably, the anti-adhesion modulator is also constituted by an epoxy polydimethylsiloxane.

As base ingredient and as adhesion modulator, it is possible to use respectively the products manufactured by the supplier Rhodia and having the following trade names respectively: UV POLY 200 and UV RCA 200. Similarly, the polymerization agent based on diaryliodonium salt can be that manufactured and sold under the trade name UV CATA 21 1 by said supplier Rhodia.

Said anti-stick agent (which serves amongst other things to enable the stripping composition to be spread easily on the walls of the mold and significantly to reduce the sticky appearance left by the epoxy polydimethylsiloxane when not polymerized) can be constituted by a mixture of a monovinyl ether and a divinyl ether.

In a preferred embodiment, the monovinyl ether is dodecyl monovinyl ether [formula CH₃—(CH₂)₁₁—O—CH═CH₂], while the divinyl ether is 1.4 cyclohexane dimethanol divinyl ether [formula CH₂═CH—O—C₆H₁₀—O—CH═CH₂].

Advantageously, said stripping composition adapted to the mold comprises:

-   -   5 to 7 parts by weight of the polymerization agent;     -   5 to 10 parts by weight of the anti-adhesion modulator, said         anti-adhesion modulator being an epoxy polydimethylsiloxane; and     -   the anti-stick agent being present at a concentration in the         range 8 to 12 parts by weight of a dodecyl monovinyl ether and 8         to 12 parts by weight of a cyclohexane dimethanol divinyl ether.

More advantageously, the stripping composition has:

-   -   6 parts by weight of the polymerization agent;     -   8 parts by weight of the anti-adhesion modulator; and     -   the anti-stick agent being present at a concentration of 11.4         parts by weight of a dodecyl monovinyl ether and 11.4 parts by         weight of a cyclohexane dimethanol divinyl ether.

Thus, by means of the invention, a solvent-free stripping composition is obtained which presents very good anti-adhesion properties, in particular because it is made on the basis of silicone. This stripping composition also presents good performance in terms of sticking behavior and painting behavior of the composite part made by molding. Because of the chemical characteristics of said composition which is based on epoxy siloxanes, the small amount that might be transferred during molding has no significant negative influence on the sticking properties or on the painting behavior of the part, contrary to that which can be observed with stripping compositions based on solvent.

It should be observed that compared with usual stripping compositions based on solvent, the composition of the invention obtained from the above-specified mixture also presents the following advantages:

-   -   elimination of the problem of dumping volatile organic         compounds;     -   reduction in the quantity of composition consumed;     -   reduction in the time required to apply the composition;     -   improvement in the sticking characteristics on the composite         material; and     -   improvement in surface appearance.

The stripping composition of the invention polymerizes under the action of ultraviolet radiation or on application of heat. The polymerization cycle by heating may comprise 1 hour at 150° C. (±5° C.).

Nevertheless, depending on the intended application, this cycle can be optimized, e.g. to 30 minutes at 100° C.

The stripping composition of the invention is liquid and it is applied to the surface of the mold at very small thickness (generally of the order of one micrometer), preferably by hand, using a cloth or by means of wipes pre-impregnated with the composition.

Generally, it is not necessary to apply the composition to the mold for each molding operation. The number of molding operations that are possible using a coating of the composition of the present invention depends on the type of molding that is performed, and it generally remains equivalent to that obtained with usual stripping compositions based on solvent.

It should be observed that the stripping composition of the invention is effective for polymerizing any composite part in molds made of metal or of composite material, using epoxy resins of a class less than or equal to 180° C. 

1-7. (canceled)
 8. A mold for making a composite material part, the mold being coated in a stripping composition comprising: 100 parts by weight of a base ingredient constituted by an epoxy polydimethylsiloxane; 0.5 to 10 parts by weight of a polymerization agent for polymerizing the base ingredient and constituted by a diaryliodonium salt; an anti-adhesion modulator constituted by a silicone polymer, present at a concentration of not more than 30 parts by weight; and an anti-stick agent making the composition less tacky prior to polymerization, constituted at least by a vinyl ether compound, which is present at a concentration of not more than 40 parts by weight.
 9. A mold according to claim 8, wherein said anti-adhesion modulator is also constituted by an epoxy polydimethylsiloxane.
 10. A mold according to claim 8, wherein said anti-stick agent is constituted by a mixture of a monovinyl ether and a divinyl ether.
 11. A mold according to claim 10 wherein said monovinyl ether is dodecyl monovinyl ether.
 12. A mold according to claim 10, wherein said divinyl ether is 1.4 cyclohexane dimethanol divinyl ether. 5 to 7 parts by weight of the polymerization agent; 5 to 10 parts by weight of the anti-adhesion modulator, said anti-adhesion modulator being an epoxy polydimethylsiloxane; and the anti-stick agent being present at a concentration in the range 8 to 12 parts by weight of a dodecyl monovinyl ether and 8 to 12 parts by weight of a cyclohexane dimethanol divinyl ether.
 14. A mold according to claim 13, wherein the stripping composition has: 6 parts by weight of the polymerization agent; 8 parts by weight of the anti-adhesion modulator; and the anti-stick agent being present at a concentration of 11.4 parts by weight of a dodecyl monovinyl ether and 11.4 parts by weight of a cyclohexane dimethanol divinyl ether.
 15. A wipe or cloth impregnated in a stripping composition presenting the characteristics of claim
 8. 16. A method of molding a composite material part, wherein the mold is coated in a stripping composition comprising: 100 parts by weight of a base ingredient constituted by an epoxy polydimethylsiloxane; 0.5 to 10 parts by weight of a polymerization agent for polymerizing the base ingredient and constituted by a diaryliodonium salt; an anti-adhesion modulator constituted by a silicone polymer, present at a concentration of not more than 30 parts by weight; and an anti-stick agent making the composition less tacky prior to polymerization, constituted at least by a vinyl ether compound, which is present at a concentration of not more than 40 parts by weight.
 17. A method according to claim 16, wherein said anti-adhesion modulator is also constituted by an epoxy polydimethylsiloxane.
 18. A method according to claim 16, wherein said anti-stick agent is constituted by a mixture of a monovinyl ether and a divinyl ether.
 19. A method according to claim 18, wherein said monovinyl ether is dodecyl monovinyl ether.
 20. A method according to claim 18, wherein said divinyl ether is 1.4 cyclohexane dimethanol divinyl ether.
 21. A method according to claim 16, wherein said stripping composition has: 5 to 7 parts by weight of the polymerization agent; 5 to 10 parts by weight of the anti-adhesion modulator, said anti-adhesion modulator being an epoxy polydimethylsiloxane; and the anti-stick agent being present at a concentration in the range 8 to 12 parts by weight of a dodecyl monovinyl ether and 8 to 12 parts by weight of a cyclohexane dimethanol divinyl ether.
 22. A method according to claim 21, wherein said stripping composition has: 6 parts by weight of the polymerization agent; 8 parts by weight of the anti-adhesion modulator; and the anti-stick agent being present at a concentration of 11.4 parts by weight of a dodecyl monovinyl ether and 11.4 parts by weight of a cyclohexane dimethanol divinyl ether.
 23. A method according to claim 16, wherein the surface of the mold is coated with the stripping composition to a thickness of micrometer order.
 24. A method according to claim 16, wherein the surface of the mold is coated with a wipe or a cloth impregnated in the stripping composition.
 25. A method according to claim 16, wherein the stripping composition is polymerized under the action of ultraviolet radiation.
 26. A method according to claim 16, wherein the stripping composition is polymerized by applying heat.
 27. A method according to claim 26, wherein the polymerization cycle is 1 hour at 150° C.±5° C.
 28. A method according to claim 26, wherein the polymerization cycle is 30 minutes at 100° C.
 29. A method according to claim 21, wherein the surface of the mold is coated with a wipe or a cloth impregnated in the stripping composition.
 30. A method according to claim 29, wherein the stripping composition is polymerized by applying heat.
 31. A method according to claim 16, in which the composite material part is a helicopter blade or an element of such a blade. 